Title :パーティクルボードとMDFの穴あけ加工における超硬合金ビットの摩耗特性
Title alternative :Wear of Cemented Carbide Bits in Machine Boring of Particleboard and MDF
Authors :番匠谷, 薫
福田, 英昭
萬谷, 哲朗
村瀬, 安英
Authors alternative :Bansyoya, Kaoru
Fukuda, Hideaki
Mantani, Tetsurou
Murase, Yasuhide
Issue Date :1-Sep-1995
Abstract :In this study, total twelve kinds of cemented carbide bits for machine boring. that is, type K bits. impact-resisting bits and micro-grained bits were prepared. And tool-life tests whose final number of boring holes of each bit was 1000 in the machine boring of particleboard and MDF (medium density fiberboard) were performed under boring conditions of 3000rpm of spindle speed, O.1mm/rev of feed per revolution and 30mm of boring depth, the progression of spur edge recession of each bit was examined. From the experimental results, the relationship of edge recessions for five kinds of type K bits (K01-K40) to edge hardeness or cobalt content was not clear. For five kinds of impact-resisting bite (V4-V6 and E1), V6 bit showed the highest edge recession and these edge recessions progressed slower as the edge hardness became higher. For two kinds of micro-grained bits(F), edge recessions showed extremely small as compared with those of type K bits and impact-resisting bits. Furthermore, it became clear that edge recessions for twelve kinds of cemented carbide bits had good correlations with edge hardness and grain diameter of tungusten carbide.
Type Local :雑誌掲載論文
ISSN :0026-8917
Publisher :日本木材加工技術協会
URI :http://hdl.handle.net/20.500.12000/1763
Citation :木材工業 Vol.50 no.9 p.413 -417
Appears in Collections:Peer-reviewed Journal Articles (Faculty of Education)

Files in This Item:

File Description SizeFormat
fukuda_h06.pdf475KbAdobe PDFView/Open