Title :The Growth and Linear-Electro-Optic Effect of Molecular Crystal: Hexamine(CH_2)_6 N_4
Authors :Takushi, Eisei
Authors alternative :沢岻, 英正
Issue Date :1-Mar-1973
Abstract :The crystal growth, optical propertiea, and electro-optic coefficients of hexamethylene-tetramine (HMT), (CH_2)_6 N_4, are described. Crystals were grown from vapor phase by controlled sublimation in an electric furnace and from alcoholic solution. Crystals were transparent from 2200 Å with the measurement in the range of ultraviolet and visible spectrum, and showed dodecahedral habit exhibiting a distinct {100} natural growth faces. Crystalline index of refraction at 20℃ was measured using microacope to be 1.57 at wavelength of 5893 Å. The electro-optic coefficient γ_<41> was found to be 0.68~1.2x 10- ^<10> cm/V for 5893 Å at room temperature. The applied voltage required to produce a phase difference of π, or one-half wavelength is about 63 KV for the crystal grown from alcoholic solution. The wavelength dependence of the electro-optic coefficients, the half-wave voltage, and the conditions for the crystal growth are discussed. Nonlinear susceptibility and the second harmonic coefficnt are estimated to be 0.6 Xl0-^<10> cm/V and the order of l0-^<10> cm/V, respectively.
Type Local :紀要論文
Publisher :琉球大学理工学部
URI :http://hdl.handle.net/20.500.12000/23493
Citation :琉球大学理工学部紀要. 理学編 = Bulletin of Science & Engineering Division, University of Ryukyus. Mathematics & natural sciences no.16 p.84 -89
Appears in Collections:No.16 (1973/03)

Files in This Item:

File Description SizeFormat
No16p084.pdf819KbAdobe PDFView/Open